团体标准
T/SPUIA0002—2021
建筑用硅烷改性弹性体密封胶
Silanemodifiedelasticsealantforbuilding
报批稿
2021-02-01实施 2021-01-20发布
上海市聚氨酯工业协会发布
全国团体标准信息平台
全国团体标准信息平台
T/SPUIA0002-2021
I目次
前言···························································································································III
1范围·························································································································1
2规范性引用文件··········································································································1
3术语和定义················································································································2
4分类和标记················································································································2
5要求·························································································································3
6试验方法···················································································································4
7检验规则···················································································································7
8标志、包装、运输和贮存······························································································8
全国团体标准信息平台
全国团体标准信息平台
T/SPUIA0002-2021
III前言
本文件按照GB/T1.1—2020《标准化工作导则第1部分:标准化文件的结构和起草规则》的方法
起草。
请注意本文件的某些内容可能涉及专利。本文件的发布机构不承担识别专利的责任。
本文件由上海市聚氨酯工业协会提出并组织实施。
本文件由上海市聚氨酯工业协会归口。
本文件起草单位:上海抚佳精细化工有限公司、杭州之江新材料有限公司、上海康达化工新材料集
团股份有限公司、浙江凌志新材料有限公司、浙江新安化工集团有限公司、广州市高士实业有限公司、
龙口德源高分子科技有限公司、山东景茂新材料有限公司、广州雷斯曼新材料科技有限公司。
本文件主要起草人:崔洪彬、黄开腾、刘伟明、蔡公华、李海平、杨静、朱瑞华、刁发进、朱超、
张福来、姚美娟、胡颖娟、曹胡亮。
本文件承诺执行单位:上海抚佳精细化工有限公司、杭州之江新材料有限公司、上海康达化工新材
料集团股份有限公司、浙江凌志新材料有限公司、浙江新安化工集团有限公司、广州市高士实业有限公
司、龙口德源高分子科技有限公司、山东景茂新材料有限公司、广州雷斯曼新材料科技有限公司。
全国团体标准信息平台
全国团体标准信息平台
T/SPUIA0002-2021
1建筑用硅烷改性弹性体密封胶
1范围
本文件规定了硅烷改性弹性体密封胶(以下简称产品)的分类、要求、试验方法、检验规则、标志、
包装、运输和贮存。
本文件适用于建筑接缝、收缩位移接缝和非收缩位移接缝用硅烷改性弹性体密封胶。
2规范性引用文件
下列文件中的内容通过文中的规范性引用而构成本文件必不可少的条款。其中,注日期的引用文件,
仅该日期对应的版本适用于本文件;不注日期的引用文件,其最新版本(包括所有的修改单)适用于本
文件。
GB/T191包装储运图示标志
GB/T1741-2007漆膜耐霉菌性测定法
GB/T7124胶粘剂拉伸剪切强度的测定(刚性材料对刚性材料)
GB/T9286—1988色漆和清漆漆膜的划格试验
GB/T13477.1建筑密封材料试验方法第1部分:试验基材的规定
GB/T13477.2建筑密封材料试验方法第2部分:密度的测定
GB/T13477.3—2017建筑密封材料试验方法第3部分:使用标准器具测定密封材料挤出性的方
法
GB/T13477.5—2002建筑密封材料试验方法第5部分:表干时间的测定
GB/T13477.6—2002建筑密封材料试验方法第6部分:流动性的测定
GB/T13477.8—2017建筑密封材料试验方法第8部分:拉伸粘结性的测定
GB/T13477.10—2017建筑密封材料试验方法第10部分:定伸粘结性的测定
GB/T13477.11—2017建筑密封材料试验方法第11部分:浸水后定伸粘结性的测定
GB/T13477.13—2019建筑密封材料试验方法第13部分:冷拉—热压后粘结性的测定
GB/T13477.17—2017建筑密封材料试验方法第17部分:弹性恢复率的测定
GB/T13477.19建筑密封材料试验方法第19部分:质量与体积变化的测定
GB/T14683—2017硅酮和改性硅酮建筑密封胶
GBT15905-1995硫化橡胶湿热老化试验方法
GB/T22083—2008建筑密封胶分级和要求
GB33372—2020胶粘剂挥发性有机化合物限量
HG/T4223—2011(2017)木地板铺装胶粘剂
JC/T485—2007建筑窗用弹性密封胶
JC/T2186—2013(2017)室内墙面轻质装饰板用免钉胶
全国团体标准信息平台
T/SPUIA0002-2021
23术语和定义
下列术语和定义适用于本文件。
3.1
硅烷改性弹性体密封胶silanemodifiedelasticsealant
以端硅烷基聚醚或端硅烷基聚氨酯为主要成分、室温固化的单组分和多组分密封胶。
4分类和标记
4.1分类
4.1.1类别
4.1.1.1产品按组分分为单组分(I)和多组分(II)两个类型。
4.1.1.2产品按用途分为三类:
F类——建筑接缝用;
R类——收缩位移接缝用;
A类——非收缩位移接缝用。
4.1.2级别
产品按GB/T22083—2008中4.2的方法对位移能力进行分级,见表1;A类产品无级别。
表1密封胶级别
级别 试验拉压幅度/% 位移能力/%
50 ±50 50.0
35 ±35 35.0
25 ±25 25.0
20 ±20 20.0
4.1.3次级别
4.1.3.1按GB/T22083—2008中规定将产品的拉伸模量分为高模量(HM)、低模量(LM)两个次
级别。
4.1.3.2A类产品无次级别。
4.2标记
产品按名称、标准编号、类型、级别、次级别顺序标记。
示例1:以符合T/SPUIA0002,多组分,收缩位移接缝用,20级,低模量的产品标记为:建筑用硅烷改性弹性体密
封胶T/SPUIA0002—Ⅱ—R—20LM。
示例2:以符合T/SPUIA0002,单组分,非收缩位移接缝用的产品标记为:建筑用硅烷改性弹性体密封胶T/SPUIA
0002—I—A。
全国团体标准信息平台
T/SPUIA0002-2021
35要求
5.1外观
产品应为细腻、均匀膏状物,无气泡、结皮和凝胶。
5.2理化性能
5.2.1F、R类产品
应符合表2规定。
表2F、R类产品理化性能指标
序号 项目技术指标
50LM50HM35LM35HM25LM25HM20LM20HM20LM-R
1 密度/(g/cm3) 规定值±0.1
2 下垂度/mm ≤1
3 表干时间/h ≤10
4挤出性a/(ml/min) ≥150
5 适用期b/min ≥60
6 弹性恢复率/% ≥80≥80≥80≥80≥70≥70≥60≥60 —
7 定伸永久变形/% — — — — — — — — >50
8拉伸模量/MPa23℃≤0.4
和
≤0.6>0.4
或
>0.6≤0.4
和
≤0.6>0.4
或
>0.6≤0.4
和
≤0.6>0.4
或
>0.6≤0.4
和
≤0.6>0.4
或
>0.6≤0.4
和
≤0.6-20℃
9 定伸粘结性 无破坏
10浸水后定伸粘结性 无破坏
11冷拉—热压后粘结性 无破坏
12 质量损失率/% ≤5
13 体积变化率/% ≤6
14 防霉等级c/级 0或1
15 涂料附着力d/级 0~2
16 耐久性等级 9030 8020 7020
17总挥发性有机物(TVOC)
/(g/L)≤40
a仅适用于单组分产品
b仅适用于多组分产品;允许采用供需双方商定的其他标值